PLA WOOD is a 3D printing filament that combines PLA with up to 40% natural wood fibers. This mixture improves strength and durability compared to conventional PLA, as well as providing an aesthetic finish similar to wood, with a rustic and authentic touch.

A minimum 0.6 nozzle is recommended

Characteristics:

-1.75m diameter.

-500 gram spool.

Properties:

- Density: 1.27 g/cm3 (ISO1183)

- Ash content: 8 %

- Melt flow index (230ºC / 2.16Kg): 19 g/10 min (ISO1133)

Mechanical properties:

- Tensile strength at break: 39 MPa (ISO 527)

- Elongation at break >3 % (ISO 527)

- Tensile modulus: 2900 MPa (ISO 527)

- Flexural modulus: 3000 MPa (ISO 178)

- IZOD impact strength, samples at 23ºC: 4 kJ/m2 (ISO 180/1A)

- IZOD impact strength, samples at -30ºC: 3 kJ/m2 (ISO 180/1A)

- Charpy impact strength, samples at 23ºC: 4 kJ/m2 (ISO 179/1eA)

Thermal properties:

- VICAT softening point B50: 70ºC (ISO 75)

- H.D.T Method A (1.82 MPa, crystallized material): 110ºC (ISO 75)